Compound Formula | ZrO2 |
Molecular Weight | 123.22 |
Appearance | White |
Melting Point | 2,715° C (4,919° F) |
Boiling Point | 4,300° C (7,772° F) |
Density | 5.68 g/cm3 |
Water absorption | <0> 0> |
Hardness | 1350 HV |
Hot expansion coefficient | 9.5×10-6 /°C |
Available capacity | 50ml, 100ml, 250ml, 500ml, 100ml, customized |
Zirconium dioxide (ZrO2), also known as zirconia, is a white crystalline oxide of zirconium. Its most naturally occurring form is the mineral baddeleyite with a monoclinic crystalline structure. Cubic zirconia is adopant stabilized cubic structured zirconia, and it can be synthesized in various colors for use as a gemstone and a diamond simulant.
* High density
* High hardness and toughness, 60 times the hardness of regular steel
* High thermal expansion
* Low thermal conductivity
* Impact resistance
* High corrosion and wear resistance
Capacity |
50ml |
100ml |
250ml |
500ml |
1000ml |
|||||
Type |
MQ |
GT |
MQ |
GT |
MQ |
GT |
MQ |
GT |
MQ |
GT |
Outer Diameter |
55mm |
65mm |
63mm |
68mm |
94mm |
91mm |
106mm |
106mm |
123mm |
120mm |
Height |
60mm |
40mm |
63mm |
60mm |
82mm |
78mm |
106mm |
96mm |
123mm |
132mm |
Wall Thickness |
6mm |
6mm |
7mm |
7mm |
8mm |
8mm |
8mm |
8mm |
8mm |
8mm |
Lid Thickness |
6mm |
6mm |
7mm |
7mm |
7mm |
7mm |
7mm |
7mm |
8mm |
8m |
The above dimensions are for your reference. Contact us for precise specifications or customized requests.
– Yttria Stabilized Zirconia / YSZ grinding jars are used to grind materials into extremely fine powder for use in mineral dressing processes, paints, pyrotechnics, ceramics and selective laser sintering.
– Zirconia jars and Zirconia balls are strong and have good abrasion resistance, which prevents mixing with other impurities while ball mill grinding.
ACM’s Yttria Stabilized Zirconia Jar with Lid is carefully handled to minimize damage during storage and transportation and to preserve the quality of our products in their original condition.